) Rotted wood impregnated with epoxy does not make the damaged wood as good as new. Deep penetration of epoxy into rotted wood will make the wood hard but it will not restore its original strength. This is not important if the rotted material is non-load bearing. A rotted door threshold does not need to be strong, just hard. However, when the wood fiber is damaged, wood loses its ability to carry loads and unless the fiber is replaced, it will not regain its full strength. A rotted deck beam or sailboat mast needs more than epoxy consolidation to return the wood to its original load carrying capacity.
2) Adhesion in all but the highest density wood is not enhanced by deep penetration of the glue into the wood. Research performed at the Forest Products Laboratory showed that adhesion to birch was increased slightly by using thinned epoxy. In lower density wood species like Sitka spruce or Douglas fir, the weak link is the cross grain strength of the wood. It does not matter if the epoxy penetrates 1/4" into the wood or 5/1000". The strength of the wood, the amount of surface area and the adhesive ability of the glue determine the strength of a glue joint. Most types of wood glue do not penetrate deeply, yet, if used properly, they can exceed the grain strength. Epoxy is no exception.
3) Water resistance of a piece of wood is not enhanced by deep penetration. Wrapping wood in plastic makes a pretty good waterproof seal without any penetration at all. Likewise, an epoxy coating on the surface is more water-resistant than a thinned epoxy coating that has penetrated deeply into the wood because, in most instances, the epoxy thinned with solvent is porous.
The USDA Forest Products Laboratory developed the Moisture Exclusion Effectiveness (MEE) test. It is a measure of how much moisture is absorbed by wood when it is continuously exposed to 100% humidity. Higher numbers mean the wood has absorbed more moisture while lower numbers indicate less moisture is absorbed. You can see that epoxy with solvent added is not nearly as moisture resistant as un-thinned epoxy (Figure 2). However, if you need an epoxy coated surface that is less of a vapor barrier, thinning WEST SYSTEM epoxy with solvent is a valid way to achieve this
___________________________________________________________________________
|| The Live-Aboard List : send a "subscribe" or "unsubscribe" request ||
|| in body of message to: ||